Formation of nanotubes on commercially pure titanium at high potentials (=10 V) and their electrochemical response

Waseem Haider, U. H. Shah, Ishraq Shabib, K. M. Deen

Research output: Contribution to journalArticlepeer-review

Abstract

The commercially pure titanium (cpTi-2) was anodized at high potentials (≥10 V) in an organic solution containing fluoride ions. The morphology of the nanotubular structure (NTs) depends on the applied electric field as evaluated from the scanning electron microscope images. The internal diameter of the NTs increased from ∼26 to ∼150 nm with the increase in potential from 10 to 60 V. The growth of Ti6O NTs along the (110) and (112) crystallographic planes and increase in crystallite size as determined from x-ray diffraction patterns is found to be a function of applied potential during the anodizing process. The electrochemical behavior of these anodized samples was evaluated in 1 wt% NaCl solution through potentiodynamic polarization and electrochemical impedance spectroscopy test methods. The NTs formed at high potentials (50 and 60 V) represented relatively smaller Tafel slopes (b a and b c) and larger corrosion (i corr) and passive (i p) current compared to NTs developed at low potentials. These results were in support with the improved kinetic response of the Ti6O film, predicted from the simulation of impedance spectra. The p-type semiconductive behavior and an order of magnitude higher charge carrier concentration were also exhibited by NTs formed at potential >40 V as confirmed from Mott Schottky analyses.

Original languageEnglish
Article number065050
JournalMaterials Research Express
Volume6
Issue number6
DOIs
StatePublished - Mar 22 2019

Keywords

  • mott schottky analyses
  • nano-tubular structure
  • titanium

Fingerprint

Dive into the research topics of 'Formation of nanotubes on commercially pure titanium at high potentials (=10 V) and their electrochemical response'. Together they form a unique fingerprint.

Cite this